SYSTEM TI 5-BLANK is a non-precious-dental milling alloy on Titanium-Aluminium-Vanadium Base.
SYSTEM TI5-BLANK is intended for the use of crowns, bridges and prosthesis.

Components-characteristics and use of Titanium Grade 5

Non-precious dental milling alloy on titanium-aluminium-vanadium base

Component of the alloy in %

• Al: 5,50 – 6,50
• V: 3,50 – 4,50
• N: max. 0,05
• Fe: max. 0,25
• O: max. 0,13
• C: max. 0,08
• H: max. 0,012
• Ti: Rest

 Characteristics

• elastic limit: 760 MPa – 850 MPa
• breaking elongation: 8 % – 14 %
• Tenacity: 825 MPa – 985 MPa
• Specific gravity: 4,4 g/cm³
• melting temperature: 1650°C +/- 50°C
• WAK (200 – 400°C): ~ 12,4 x10-6K-1
• Hardness after casting:: 310 HV 10 +/- 41°C
• Firing temperature: approx. 980 °C
• System TI 5-Blank consists of a Titanium -Aluminium-Vanadium-alloy.

System TI 5-Blank

System TI 5-Blank is intended for the use of crowns, bridges and framework and only intended for use in the DENTAL FIELD.

Lasering / Welding:

Only with lasering- or plasma device with TIG technology. If required, use a pure Titanium thread grade 1 with Ø = 1,0 –0,25 mm and / or a pure Titanium plate grade 1 with Ø = 0,5 or 0,25 mm.

Ceramic Firing:

Use low-melting ceramics only and follow the manufacturer´s specification.